第一、拉力的范圍

  萬能拉力試驗機裸電線拉力試驗方法主要用來測試電線等各種金屬導體和裸電線的拉伸性能。測試的方法就是用一定長度的夾具承受遞增的拉力，知道斷裂為止。

First, the scope of force

The tensile properties of universal tensile testing machine bare wire pull test method is mainly used for testing of wire and other metal conductor and bare wire. Test method for a certain length of the fixture is under increasing tensile fracture, know so far.

第二、試驗的設(shè)備

拉力試驗機，它的誤差不大于正負百分之一。

Second, test equipment

Tensile testing machine, its error is not more than plus or minus one percent.

第三、試驗的準備

@1、實芯導體

    1.取樣：準備合格的樣品3根，取樣的時候，要避免試件受到拉伸、彎曲、扭轉(zhuǎn)或者其他的損壞。

    2.矯直試件：細心的用手進行矯正，必要的時候可以用木槌輕輕的敲直，測試拉壓強度的時候，可以不用矯直。

    3. 標出標距長度：在試驗的夾具中部標出標距長度200mm。不能夠使試件提早的斷裂，線條應(yīng)該是清晰的。標距長度的誤差：硬線試件為正負0.2mm，軟線試件為正負0.5mm。

Third, test preparation

@1, solid core conductor

1 sampling: prepare samples qualified 3, sampling time, to avoid the specimen under tensile,bending and torsion or other damage.

2 straightening specimen: careful manual correction, when necessary, can use the gavel knock lightly straight, when testing the tensile and compressive strength, can not straightening.

3 mark the gauge length: mark in the middle clamp test gauge length 200mm. Can't makespecimens of early fracture lines should be clear. Standard error of length: hard wire specimens for positive and negative 0.2mm, cord specimens for positive and negative 0.5mm.

@2、絞合導體

    1.取樣：從外觀檢查合格的樣品中截取試件3根，試件長度為原始標距長度加兩倍鉗口夾持長度。

    2.試件加工：解開試件兩端的股線，分開并彎成圓鉤形，清洗后，用低熔合金或樹脂澆灌椎體端頭。也可用壓接法或夾具法制作。

@2, a stranded conductor

1 sampling: samples from visual inspection qualified from 3 specimens, the length of the specimen to the original gauge length of two times the jaw clamping length.

2 specimen processing: Unlock the specimen at both ends of the wire, and bent into a circledivided hook, after cleaning, using low melting alloy or resin on vertebral end. Also availablecrimping method or clamp method.

@3、試驗步驟

    1.將試件夾持在萬能拉力試驗機的鉗口內(nèi)，標志線應(yīng)露出在鉗口處。夾緊后試件的位置應(yīng)保證試件的縱軸與拉伸的中心線重合。

    2.選定拉伸速度

    3.啟動萬能拉力試驗機，加載必須平穩(wěn)，速度均勻，無沖擊。

    4.當試件被拉伸斷裂后，讀數(shù)并記錄負荷，取三五有效數(shù)。取下試件將斷口小心對齊，擠緊，測量并記錄最終標距長度。